sh/t 0536-1993 / sh/t 0537-1993 
brief introduction
product characteristics and application: hfgel-120v series quaternary ammonium cation modified organic bentonite and dedicated as naphthenic oils, paraffinic mineral oil and synthetic oil thickening agent, has good thickening property, corrosion resistance and high temperature performance. both can be single  hfgel-120v of organic bentonite and bentonite dispersion in base oil made from bentonite bentonite grease, can also be used as graphite, molybdenum disulfide as a solid lubricant in the oil carrier thickener, suspending agent.  hfgel-120v organic bentonite, which was modified by three times. not containing quartz, feldspar and other hard impurities, wear low. made of grease is suitable for high speed, high load and precision machinery lubrication, long-term in high temperature of 150 deg c and its resistance to temperature is better than the traditional lithium grease, urea grease polymerization with molybdenum disulfide grease. hfgel-120-v can also be used for the preparation of cable with grease
  • physical indicators
  • applications
  • instructions
  • packing and storage

exterior

beige fine powder

105 ℃ volatile

≤3.5%

size (over 200 mesh)

≥98%

proportion(g/cm³)

1.65

bulk density(kg/m³)

≤400

  naphthenic oil and paraffin base mineral oil based bentonite bentonite grease; poly & alpha; olefins, esters, glycol, alkylation of aromatic hydrocarbon synthetic base oil lubrication grease and vegetable oil as base oil of lubricating grease.
when the product is used in grease required polar activators include: dry acetone, ethanol / water (95/5), when production requires high shear to achieve the desired expansion, the specific use:
(1) in the opening of the kettle, 1/2 of the total base oil added to the reactor was heated to 60 ~ 70 ℃;
(2) was added while stirring hfgel-120-v (8-15% of the total formulation, the use of synthetic oil is higher than the amount of mineral oil) was stirred for 5 to 10 minutes;
(3) addition of a polar activator (20 to 40%, the amount of organic soil), and then adding other desired additives, stirred for 25 to 30 minutes
(4) then the remaining half of the base oil was added to the reactor, stirred for 1-2 hours;
(5) with colloidal pump it through a three-roll mill or shearing machine;
(6) in addition to gas, filtered, packaged lubricants.
such as increasing the dispersion rate and prolong the dispersion time and raise the temperature will increase the use of results fhgel-120-v.
outside the package of kraft paper bag, the inner packing uses the double layer packing of the polyethylene film bag, or the paper bag packing, the weight is usually 25 0.25kg, or by the user request packing. under the condition of dry condition, the temperature is 0~30, and the quality is 24 months.